022Cr19Ni13Mo3
022Cr19Ni13Mo3 is a grade designated under GB. Its recorded composition includes C ≤ 0.03%, Cr 18–20%, Mn ≤ 2%, Ni 11–15% and Mo 3–4%. No cross-standard equivalents are recorded for this grade yet.
- Designations 1
Chemical composition
8 elements on file · weight %What this alloy is
Logarithmic scale, 0.01 % to 100 % — every value here compares directly, decade by decade.
| Element | % by weight |
|---|---|
≤ 0.03 | |
≤ 1 | |
≤ 2 | |
≤ 0.045 | |
≤ 0.03 | |
18–20 | |
3–4 | |
11–15 |
The scale is logarithmic, not the element’s raw share of the alloy — the only honest way to fit 0.01 % and 100 % in one picture, and it means every value here can be compared with every other.
| Element | As publishedsource text, verbatim | Min% by weight | Max% by weight | Bound |
|---|---|---|---|---|
| C | ≤0.03 | — | 0.030 | Max |
| Si | ≤1 | — | 1.000 | Max |
| P | ≤0.045 | — | 0.045 | Max |
| S | ≤0.03 | — | 0.030 | Max |
| Cr | 18-20 | 18.000 | 20.000 | Range |
| Mn | ≤2 | — | 2.000 | Max |
| Ni | 11-15 | 11.000 | 15.000 | Range |
| Mo | 3-4 | 3.000 | 4.000 | Range |
The published column is the source string byte-for-byte, decimal comma and all; Min and Max are the parsed bounds. Elements not listed have no value on file — they are omitted, never inferred.
Predicted transformation temperatures
This grade's composition falls outside the published model's validated range (a low-alloy composition window), so no transformation temperature is predicted here.
Physical & mechanical properties
An absent property means we hold no value for it — it is left out rather than estimated, interpolated from a neighbouring grade, or filled from a handbook. It does not mean the property is undefined for the material.
Heat treatment
Supply condition
- Solution annealingSteel product
- Solution annealing
Conditions the standard permits on delivery. No temperature or medium is published for these, so no order and no alternation is implied.
Source: www.caishuku.com
Looking for this grade under another name?
Search the catalogue by designation, material number or composition — every name on this page is itself a way in.