85Cr17
85Cr17 is a grade designated under GB. Its recorded composition includes C 0.75–0.95%, Si ≤ 1%, Cr 16–18%, Mn ≤ 1% and Mo ≤ 0.75%. No cross-standard equivalents are recorded for this grade yet. Recorded mechanical properties include HB ≤ 255.
- Designations 1
Chemical composition
8 elements on file · weight %What this alloy is
Logarithmic scale, 0.01 % to 100 % — every value here compares directly, decade by decade.
| Element | % by weight |
|---|---|
0.75–0.95 | |
≤ 1 | |
≤ 1 | |
≤ 0.04 | |
≤ 0.03 | |
16–18 | |
≤ 0.75 | |
≤ 0.6 |
The scale is logarithmic, not the element’s raw share of the alloy — the only honest way to fit 0.01 % and 100 % in one picture, and it means every value here can be compared with every other.
| Element | As publishedsource text, verbatim | Min% by weight | Max% by weight | Bound |
|---|---|---|---|---|
| C | 0.75-0.95 | 0.750 | 0.950 | Range |
| Si | ≤1 | — | 1.000 | Max |
| P | ≤0.04 | — | 0.040 | Max |
| S | ≤0.03 | — | 0.030 | Max |
| Cr | 16-18 | 16.000 | 18.000 | Range |
| Mn | ≤1 | — | 1.000 | Max |
| Ni | ≤0.6 | — | 0.600 | Max |
| Mo | ≤0.75 | — | 0.750 | Max |
The published column is the source string byte-for-byte, decimal comma and all; Min and Max are the parsed bounds. Elements not listed have no value on file — they are omitted, never inferred.
Predicted transformation temperatures
This grade's composition falls outside the published model's validated range (a low-alloy composition window), so no transformation temperature is predicted here.
Physical & mechanical properties
An absent property means we hold no value for it — it is left out rather than estimated, interpolated from a neighbouring grade, or filled from a handbook. It does not mean the property is undefined for the material.
Properties by condition
0 conditions · 0 values1 further values are held for this grade under a condition the source did not name — a bound with no quantity attached. They are withheld rather than shown against a guessed condition.
Looking for this grade under another name?
Search the catalogue by designation, material number or composition — every name on this page is itself a way in.