15MnCrMo3-2

15MnCrMo3-2 is a material in the category High-strength steels, held under material number 1.8719. Its recorded composition includes C 0.1–0.2%, Cr 0.4–0.65%, Mn 0.6–1%, Ni 0.7–1% and Mo 0.4–0.6%. No cross-standard equivalents are recorded for this grade yet. Its recorded density is 7.85 g/cm³.

Material no. 1.8719
Category High-strength steels · 128 grades
Designations 1

Search Inquiry Datasheet as PDFPrint-ready A4 documentGenerating …Download startedTry again

About High-strength steels

High-strength steels are steels designed to carry high loads while resisting deformation. They are used for load-bearing structures, vehicles and machinery where strength, durability and reduced material weight are important.

This describes the material class as a whole. Always confirm the individual grade against the standard before ordering.

Chemical composition

11 elements on file · weight %

What this alloy is

Iron — the balance, never listed by a standard — 96.5 %Ni — 0.9 %Mn — 0.8 %Cr — 0.5 %Traces & impurities · 1.3 %

Logarithmic scale, 0.01 % to 100 % — every value here compares directly, decade by decade.

Element	% by weight
	0.1–0.2
	0.15–0.35
	0.6–1
	0.025
	0.025
	0.4–0.65
	0.4–0.6
	0.7–1
	0.03–0.08
	0.15–0.5
	≥ 0.0005

0.01 %0.1 %1 %10 %100 %

The scale is logarithmic, not the element’s raw share of the alloy — the only honest way to fit 0.01 % and 100 % in one picture, and it means every value here can be compared with every other.

Element	As publishedsource text, verbatim	Min% by weight	Max% by weight	Bound
B	≥0,0005	0.001	—	Min
C	0,10-0,20	0.100	0.200	Range
Si	0,15-0,35	0.150	0.350	Range
P	0,025	0.025	0.025	Exact
S	0,025	0.025	0.025	Exact
V	0,03-0,08	0.030	0.080	Range
Cr	0,40-0,65	0.400	0.650	Range
Mn	0,60-1,00	0.600	1.000	Range
Ni	0,70-1,00	0.700	1.000	Range
Cu	0,15-0,50	0.150	0.500	Range
Mo	0,40-0,60	0.400	0.600	Range

The published column is the source string byte-for-byte, decimal comma and all; Min and Max are the parsed bounds. Elements not listed have no value on file — they are omitted, never inferred.

Predicted transformation temperatures

computed from composition · °C

Predicted Ae3801°C

Predicted Ae1717°C

Predicted Acm444°C

Predicted Bs529°C

These four temperatures are a CALCULATION from this grade's own composition, using the published Li, Niebuhr, Meekisho & Atteridge (1998) model — never a measurement, and computed from the UPPER BOUND of each element's specified range, not a mid-range figure. Where this grade also has a measured transformation point (Ac1, Ac3, Ar1, Ar3) on file, it is shown separately, in Physical & mechanical properties, and is never replaced by the predicted figures here — Ae (predicted, equilibrium) and Ac/Ar (measured, on heating or cooling) are different physical quantities and can differ by tens of degrees; a mismatch between the two is not an error in either.

Physical & mechanical properties

Density7,85g/cm³Exact

An absent property means we hold no value for it — it is left out rather than estimated, interpolated from a neighbouring grade, or filled from a handbook. It does not mean the property is undefined for the material.

Similar grades — and why

Selection rule, stated so you can disagree with it: same number class 1.8, a shared category, and a published range for Ni / Mn that overlaps this grade’s. These are neighbours in composition space — they are not equivalents, and none is claimed to be interchangeable with this grade.

S690G1QL1.8920

Ni 0,70-1,00 · Mn 0,60-1,00