DIN / EN · Europe · 2 designations

PMHS2-2-2

PMHS2-2-2 is a material in the category High-speed steels, held under material number 1.3397. Its recorded composition includes C 0.55–0.65%, V 1.4–1.8%, Cr 3.8–4.5%, Mo 1.8–2.4% and W 1.9–2.5%. We list one designation recorded for this grade, in the standard DIN / EN. Its recorded density is 7.85 g/cm³.

Material no. 1.3397
Category High-speed steels · 59 grades
Designations 2

Search Inquiry Datasheet as PDFPrint-ready A4 documentGenerating …Download startedTry again

About High-speed steels

High-speed steels are alloyed tool steels designed to retain hardness and cutting ability when tools heat up during high-speed machining. Their hot hardness and wear resistance make them suitable for cutting tools such as drills, milling cutters, taps and broaches.

This describes the material class as a whole. Always confirm the individual grade against the standard before ordering.

Also known as

2 designations · 1 standards · nothing hidden

This grade’s own namerecorded in our sources as this grade’s own designation under that standard.

Indicativetaken from a published cross-reference table; a close match, not a guarantee of interchangeability. Verify against the mill certificate before ordering.

Withdrawndesignation no longer current — a separate column from the two above, so a name can be same grade and withdrawn at once.

DIN / ENEurope · 2

ASP2012This grade’s own nameWithdrawn
PMHS2-2-2This grade’s own name

Every designation on file is listed — no truncation, no “+ n more”. Each one is itself a route that leads back here.

Chemical composition

9 elements on file · weight %

What this alloy is

Iron — the balance, never listed by a standard — 88 %Cr — 4.2 %W — 2.2 %Mo — 2.1 %Traces & impurities · 3.6 %

Logarithmic scale, 0.01 % to 100 % — every value here compares directly, decade by decade.

Element	% by weight
	0.55–0.65
	0.8–1.2 —
	0.2–0.4
	0.03
	0.03
	3.8–4.5
	1.8–2.4
	1.4–1.8
	1.9–2.5

0.01 %0.1 %1 %10 %100 %

The scale is logarithmic, not the element’s raw share of the alloy — the only honest way to fit 0.01 % and 100 % in one picture, and it means every value here can be compared with every other.

Element	As publishedsource text, verbatim	Min% by weight	Max% by weight	Bound
C	0,55-0,65	0.550	0.650	Range
Si	0,80-1,20	0.800	1.200	Range
P	0,03	0.030	0.030	Exact
S	0,03	0.030	0.030	Exact
V	1,40-1,80	1.400	1.800	Range
Cr	3,80-4,50	3.800	4.500	Range
Mn	0,20-0,40	0.200	0.400	Range
Mo	1,80-2,40	1.800	2.400	Range
W	1,90-2,50	1.900	2.500	Range

The published column is the source string byte-for-byte, decimal comma and all; Min and Max are the parsed bounds. Elements not listed have no value on file — they are omitted, never inferred.

Predicted transformation temperatures

Not enough recorded composition to predict a transformation temperature for this grade — missing: Ni.

Physical & mechanical properties

Density7,85g/cm³Exact

An absent property means we hold no value for it — it is left out rather than estimated, interpolated from a neighbouring grade, or filled from a handbook. It does not mean the property is undefined for the material.

Similar grades — and why

Selection rule, stated so you can disagree with it: same number class 1.3, a shared category, and a published range for Cr / W that overlaps this grade’s. These are neighbours in composition space — they are not equivalents, and none is claimed to be interchangeable with this grade.

PMHS3-3-41.3377

Cr 3,80-4,50 · W 2,30-2,80