STHG31
STHG31 is a grade designated under KS. Its recorded composition includes C 0.35–0.4%, Si 0.1–0.5%, Cr 0.3–0.6%, Mn 1.2–1.5% and Ni 0.5–1%. No cross-standard equivalents are recorded for this grade yet.
- Designations 1
Chemical composition
8 elements on file · weight %What this alloy is
Logarithmic scale, 0.01 % to 100 % — every value here compares directly, decade by decade.
| Element | % by weight |
|---|---|
0.35–0.4 | |
0.1–0.5 | |
1.2–1.5 | |
≤ 0.03 | |
≤ 0.03 | |
0.3–0.6 | |
0.15–0.25 | |
0.5–1 |
The scale is logarithmic, not the element’s raw share of the alloy — the only honest way to fit 0.01 % and 100 % in one picture, and it means every value here can be compared with every other.
| Element | As publishedsource text, verbatim | Min% by weight | Max% by weight | Bound |
|---|---|---|---|---|
| C | 0.35 - 0.4 | 0.350 | 0.400 | Range |
| Si | 0.1 - 0.5 | 0.100 | 0.500 | Range |
| P | max 0.03 | — | 0.030 | Max |
| S | max 0.03 | — | 0.030 | Max |
| Cr | 0.3 - 0.6 | 0.300 | 0.600 | Range |
| Mn | 1.2 - 1.5 | 1.200 | 1.500 | Range |
| Ni | 0.5 - 1 | 0.500 | 1.000 | Range |
| Mo | 0.15 - 0.25 | 0.150 | 0.250 | Range |
The published column is the source string byte-for-byte, decimal comma and all; Min and Max are the parsed bounds. Elements not listed have no value on file — they are omitted, never inferred.
Predicted transformation temperatures
computed from composition · °CThese four temperatures are a CALCULATION from this grade's own composition, using the published Li, Niebuhr, Meekisho & Atteridge (1998) model — never a measurement, and computed from the UPPER BOUND of each element's specified range, not a mid-range figure. Where this grade also has a measured transformation point (Ac1, Ac3, Ar1, Ar3) on file, it is shown separately, in Physical & mechanical properties, and is never replaced by the predicted figures here — Ae (predicted, equilibrium) and Ac/Ar (measured, on heating or cooling) are different physical quantities and can differ by tens of degrees; a mismatch between the two is not an error in either.
Physical & mechanical properties
An absent property means we hold no value for it — it is left out rather than estimated, interpolated from a neighbouring grade, or filled from a handbook. It does not mean the property is undefined for the material.
Looking for this grade under another name?
Search the catalogue by designation, material number or composition — every name on this page is itself a way in.