STAS steel grades — 203 designations
Every grade designated under STAS, with the material number it maps to, what kind of steel it is, its carbon window and how many other standards carry it. Open a grade for its full composition, properties and its designations in other standards. Every name on this page is an indicative cross-reference, not an asserted identity: the grades are close, not interchangeable. Check the composition before you substitute.
Also known as
203 designations| Grade | Material no. | Category | C% by weight | Also inother standards |
|---|---|---|---|---|
| 105MnCrW11 | 1.2419 | Tool steels for cold work | 1–1.1 | 16 |
| 10AlCr180 | 1.4742 | Heat resistant steels | ≤ 0.12 | 17 |
| 10Cr130 | 1.4006 | Stainless steels | 0.08–0.15 | 26 |
| 10CrMo10 | 1.7380 | Heat-resistant structural steels | 0.08–0.14 | 20 |
| 10MoCr50 | 1.7362 | Hydrogen resistant steels | 0.1–0.15 | 13 |
| 10TiNiCr180 | 1.4541 | Stainless steels | ≤ 0.08 | 25 |
| 12C130 | 1.4006 | Stainless steels | 0.08–0.15 | 26 |
| 12MoCr22 | 1.7380 | Heat-resistant structural steels | 0.08–0.14 | 20 |
| 12NiCr250 | 1.4845 | Heat resistant steels | ≤ 0.1 | 21 |
| 12SiCrNi360 | 1.4864 | Heat resistant steels | ≤ 0.15 | 14 |
| 12SiCrNi360 | 1.4886 | Others | ≤ 0.15 | 11 |
| 12SiCrNi360 | 1.4862 | Heat resistant steels | ≤ 0.1 | 6 |
| 12TiNiCr180 | 1.4541 | Stainless steels | ≤ 0.08 | 25 |
| 13CrNi30q | 1.5732 | Case hardening steels | 0.1–0.17 | 13 |
| 14CrMo4 | 1.7262 | Case hardening steels | 0.13–0.17 | 18 |
| 14CrMo4 | 1.7335 | Heat-resistant structural steels | 0.08–0.18 | 22 |
| 15Cr9q | 1.7015 | Case hardening steels | 0.12–0.18 | 15 |
| 15SiNiCr200 | 1.4828 | Heat resistant steels | ≤ 0.2 | 20 |
| 15SiNiCr200 | 1.4833 | Heat resistant steels | ≤ 0.15 | 15 |
| 16SiMn4 | 1.0445 | Higher strength steels | — | 12 |
| 17MnCr10 | 1.7131 | Case hardening steels | 0.14–0.19 | 24 |
| 18CrNi20 | 1.5920 | Case hardening steels | 0.15–0.2 | 6 |
| 18MnCr10q | 1.7131 | Case hardening steels | 0.14–0.19 | 24 |
| 18MnCr11 | 1.7131 | Case hardening steels | 0.14–0.19 | 24 |
| 205Cr115 | 1.2060 | Tool steels for cold work | 1–1.1 | 15 |
| 20MnCr12 | 1.7131 | Case hardening steels | 0.14–0.19 | 24 |
| 20MoCr130 | 1.4120 | Stainless steels | 0.17–0.22 | 3 |
| 20MoCr130 | 1.4120 | Others | 0.17–0.22 | 2 |
| 20MoCr130 | 1.4921 | High-temperature steels | 0.15–0.23 | 2 |
| 21MoMnCr12 | 1.7243 | Case hardening steels | 0.15–0.21 | 12 |
| 21MoMnCr12 | 1.3566 | Others | 0.12–0.18 | 8 |
| 24 MoCrNiMn 15z | 1.6541 | Quenched and tempered steels | 0.2–0.26 | 3 |
| 24 MoCrNiMn 15z | 1.6540 | Others | 0.2–0.26 | 4 |
| 24 MoCrNiMn 15z | 1.6758 | Quenched and tempered steels | 0.2–0.26 | 3 |
| 26MoCr11 | 1.7220 | Quenched and tempered steels | 0.3–0.37 | 24 |
| 26MoCr11 | 1.7218 | Quenched and tempered steels | 0.22–0.29 | 25 |
| 2MoNiCr175 | 1.4404 | Stainless steels | ≤ 0.03 | 25 |
| 2TiMoCr180 | 1.4521 | Stainless steels | ≤ 0.025 | 9 |
| 2TiMoCr180 | 1.4605 | Heat resistant steels | ≤ 0.03 | 8 |
| 2TiMoCr180 | 1.4523 | Others | ≤ 0.03 | 8 |
| 2TiMoCr180 | 1.4321 | Others | ≤ 0.03 | 8 |
| 30VCrW85 | 1.2581 | Tool steels for hot work | 0.25–0.35 | 18 |
| 31VCr5 | 1.2208 | Tool steels for cold work | 0.28–0.35 | 4 |
| 31VMoCr29 | 1.2365 | Tool steels for hot work | 0.28–0.35 | 18 |
| 33MoCr11 | 1.7220 | Quenched and tempered steels | 0.3–0.37 | 24 |
| 34MoCr11 | 1.7220 | Quenched and tempered steels | 0.3–0.37 | 24 |
| 34MoCr11AS | 1.7220 | Quenched and tempered steels | 0.3–0.37 | 24 |
| 34MoCr11q | 1.7220 | Quenched and tempered steels | 0.3–0.37 | 24 |
| 34MoCrNi15 | 1.6582 | Quenched and tempered steels | 0.3–0.38 | 25 |
| 34MoCrNi15q | 1.6582 | Quenched and tempered steels | 0.3–0.38 | 25 |
This grade’s own name — recorded in our sources as this grade’s own designation under that standard.
Indicative — taken from a published cross-reference table; a close match, not a guarantee of interchangeability. Verify against the mill certificate before ordering.
Withdrawn — designation no longer current — a separate column from the two above, so a name can be same grade and withdrawn at once.