DIN / EN · Europe · 2 designations

20CrMoS2

20CrMoS2 is a designation in DIN / EN for the material held under material number 1.7311, also listed as 20CrMo2. It is a material in the category Case hardening steels. We list 2 designations recorded for this grade, in the standards DIN / EN.

Material no. 1.7311
Category Case hardening steels · 60 grades
Designations 2

Search Inquiry Datasheet as PDFPrint-ready A4 documentGenerating …Download startedTry again

About Case hardening steels

Case hardening steels are steels designed to develop a hard, wear-resistant surface while retaining a tough and ductile core. They are used for components such as gears, shafts and other machine parts exposed to contact wear and cyclic loading.

This describes the material class as a whole. Always confirm the individual grade against the standard before ordering.

Also known as

2 designations · 1 standards · nothing hidden

This grade’s own namerecorded in our sources as this grade’s own designation under that standard.

Indicativetaken from a published cross-reference table; a close match, not a guarantee of interchangeability. Verify against the mill certificate before ordering.

Withdrawndesignation no longer current — a separate column from the two above, so a name can be same grade and withdrawn at once.

DIN / ENEurope · 2

20CrMo2This grade’s own nameWithdrawn
20CrMoS2This grade’s own name

Every designation on file is listed — no truncation, no “+ n more”. Each one is itself a route that leads back here.

Chemical composition

7 elements on file · weight %

What this alloy is

Iron — the balance, never listed by a standard — 97.8 %Mn — 0.7 %Cr — 0.6 %Mo — 0.4 %Traces & impurities · 0.5 %

Logarithmic scale, 0.01 % to 100 % — every value here compares directly, decade by decade.

Element	% by weight
	0.18–0.23
	0.15–0.35
	0.6–0.8
	0.035
	0.02–0.04
	0.5–0.7
	0.3–0.4

0.01 %0.1 %1 %10 %100 %

The scale is logarithmic, not the element’s raw share of the alloy — the only honest way to fit 0.01 % and 100 % in one picture, and it means every value here can be compared with every other.

Element	As publishedsource text, verbatim	Min% by weight	Max% by weight	Bound
C	0,18-0,23	0.180	0.230	Range
Si	0,15-0,35	0.150	0.350	Range
P	0,035	0.035	0.035	Exact
S	0,020-0,040	0.020	0.040	Range
Cr	0,50-0,70	0.500	0.700	Range
Mn	0,60-0,80	0.600	0.800	Range
Mo	0,30-0,40	0.300	0.400	Range

The published column is the source string byte-for-byte, decimal comma and all; Min and Max are the parsed bounds. Elements not listed have no value on file — they are omitted, never inferred.

Predicted transformation temperatures

Not enough recorded composition to predict a transformation temperature for this grade — missing: Ni.

Physical & mechanical properties

Density7,85g/cm³Exact

An absent property means we hold no value for it — it is left out rather than estimated, interpolated from a neighbouring grade, or filled from a handbook. It does not mean the property is undefined for the material.

Similar grades — and why

Selection rule, stated so you can disagree with it: same number class 1.7, a shared category, and a published range for Mn / Cr that overlaps this grade’s. These are neighbours in composition space — they are not equivalents, and none is claimed to be interchangeable with this grade.

20MoCrS31.7319

Mn 0,60-0,90 · Cr 0,40-0,70