Aging resistant steels
Aging-resistant steel is formulated to limit changes in its mechanical properties during storage and service. Its stable behavior over time makes it suitable for structural and formed components where consistent performance is important.
| Grade | Material no. | C | Si | P | S | Mn | V |
|---|---|---|---|---|---|---|---|
| P280GH | 1.0426 | 0,08-0,20 | ≤0,40 | 0,025 | 0,015 | 0,90-1,50 | ≤0,02 |
| A 516 Grade 60 | 1.9417 | ≤0,21 | 0,15-0,40 | 0,035 | 0,035 | 0,60-1,20 | — |
Standards covering this category
18Property ranges
2| Property | Unit | Min | Max | Grades |
|---|---|---|---|---|
| ReH | N/mm² | 255 | 280 | 1 |
| rho | g/cm³ | 7.85 | 7.85 | 2 |
Derived from 2 grades in this category with a recorded value.
Composition range
11| Property | Unit | Min | Max | Grades |
|---|---|---|---|---|
| C | % | 0.08 | 0.21 | 2 |
| Si | % | 0.15 | 0.4 | 2 |
| P | % | 0.025 | 0.035 | 2 |
| S | % | 0.015 | 0.035 | 2 |
| V | % | 0.02 | 0.02 | 1 |
| Cr | % | 0.3 | 0.3 | 1 |
| Mn | % | 0.6 | 1.5 | 2 |
| Ni | % | 0.3 | 0.3 | 1 |
| Cu | % | 0.3 | 0.3 | 1 |
| Nb | % | 0.01 | 0.01 | 1 |
| Mo | % | 0.08 | 0.08 | 1 |
Derived from 2 grades in this category with a recorded value.